Polyseal PS PG
2 part pouring grade polysulphide joint sealant
Properties
- Highly resilient with excellent recovery characteristics
- Provides permanent and uniform watertight seal
- Non-staining
- Excellent resistance to fatigue and stays flexible throughout its service life–won’t become brittle, caulk or crack due to ultra violet exposure
- Prevents uncontrolled cracking by allowing expansion and contraction during temperature changes
- Excellent adhesion to most common building substrates
- Good resistance to ageing. Retains joint soundness once cured
- Resistance against mild chemicals, hydrocarbon fuels, sea water
- Non-toxic. Can be used in potable water applications, swimming pools
Description
Polyseal PS PG is a two component pourable, self leveling polysulphide resin based joint sealant. Polyseal PS PG is specifically designed to be used as a watertight seal for moderate movement and control joints in horizontal areas. It is based on a liquid polysulphide polymer which when mixed with the hardener, cures to form a tough, flexible and non staining rubber like seal. Polyseal PS PG has excellent adhesion to concrete, stone, metals and other common building surfaces. The cured sealant has good resistance to most environmental chemicals & resists deterioration on prolonged exposure to UV. Polyseal PS PG is suitable for use in horizontal areas with a maximum slope gradient of 10%. The sealant has a movement accomodation factor (maf) of ±25%.
TDS for Polyseal PS PG
- Step by Step
Joint preparation
The joint edges must be clean, dry and free from oil, loose particles, cement laitance and other contaminants which may affect the adhesion. A thorough wire brushing, grinding, sand blasting or solvent cleaning may be required to expose a clean and sound substrate.The compressible joint filler shall be cut back to expose a uniform joint depth..
Priming
Primer shall be applied to a clean and dry surface prior to the installation of backer rod or bond breaking tape. Polyprime PS* is recommended to be applied on porous substrates. For non-porous substrates such as steel or glass Polyprime NP* is recommended for optimum adhesion. The primer shall be applied by a brush in a thin coat application and shall be allowed to become tack free prior to the application of the sealant. The joint edges shall be re-primed if the sealant installation is not carried out within 3 hours of application of the primer. For obtaining a clean and neat finish, masking tape shall be applied on both the edges of the joint before applying the primer.
Back-up Material
A bond breaking backing rod (Polyrod)* shall be inserted into all movement joints to avoid a three sided adhesion. Use of a backing rod will ensure proper joint depth and at the same time facilitating the formation of an hour glass profile on the applied sealant. The backer rod will also provide resistance to sealant tooling pressure and help to attain proper wetting of the substrate when the sealant is being tooled. The diameter of the backing rod shall be at least 20% larger but not greater than 33% of the joint width. This will ensure that the backer rod remains in compression and in place during sealant installation. For static and joints where the depth is not sufficient for the use of the backing rod, a bond breaking tape may be applied to prevent the three side adhesion.
Mixing & Application
POLYSEAL PS PG is supplied in pre-weighed two parts pack which requires on site mixing. pour the hardener (part B) into the base (part a) pail and mix thoroughly with a slow speed drill (300-400 rpm) fitted to a flat bladed paddle for 1-2 minutes till a uniform colour and consistency is achieved.
DO NOT PART MIX. since the base and the curing agent ratio controls the ultimate physical properties like adhesion, durability and strength, one complete kit has to be mixed at a time. the side and base of the container shall be periodically scrapped with a scrapper to ensure that the curing agent is properly dispersed and blended in the mix. pour the mixed material directly into the joint from the pail. Once the sealant has been installed a suitable rounded tool soaked in soapy water can be used to achieve an hour glass profile. any masking tape applied should be removed immediately after the sealant is installed.